Effects Paints
Effects Paints
APPLICATION AREA
Metalium Effect is used for interior wall decoration in buildings.
-The appearance of varying color shades is contingent on the characteristics of the metal powder within it.
-Its unique resin structure helps prevent the formation of bacteria and fungus.
-Application and the desired effect are achieved using a steel trowel.
-The product can be sanded to perfection.
-Its metallic properties impart a high level of brightness and a mirror-like finish.
-Metalium Effect consists of two components, A and B, along with various metal powders.
-Prior to application, ensure that all surface contaminants, such as dirt, oil, peeling paint, and dust, are removed.
-Correct any surface imperfections using San Deco Acrylic Putty Interior.
-For surfaces with existing paint or those intended for painting, it is recommended to apply a coat of San Deco Uniprimer as an undercoat.
-Combine the A and B components in an empty container and stir for 3 minutes. Gradually add the metal dust while stirring.
-Utilize a hand mixer for thorough stirring until a homogeneous mixture is achieved.
-After completing the stirring process, apply the product within 30 to 60 minutes.
-Use a steel trowel for application to achieve the desired effect.
-Once the product has set and dried at room temperature (typically around 24-48 hours), proceed with sanding.
-The sanding process involves a total of 8 different sandpaper sizes, progressing from coarse to fine, in 3 stages.
-Remove any dust remaining on the surface between each sanding stage with a dry cloth. Once the desired level of polishing is achieved, clean the surface with a dry cloth.
-For enhanced brightness and surface reflection, Metallium Effect Wax can be applied after the polishing process is completed.
-As the metal powders used are natural, any minor variations in powder color do not result in noticeable tone differences in the final product.
-Ensure that the application environment maintains a temperature between +5°C to +35°C for 24 hours during and after the application process.
Allow 24 hours for the surface to become touch-dry and 48 hours for complete drying to occur under environmental conditions of 20°C – 25°C.
Depending on the surface’s smoothness, porosity, and the chosen application method, the consumption of coating materials (comprising both A and B components and metal powder) for 1 kg of product can be estimated as follows: